Home > Products > Austenitic

SS316 / 1.4435

316 bar can be supplied, providing a high quality precision ground bar to close tolerances. Also available in plate which can be supplied as 316 plasma cut pieces and sheet which can be supplied guillotined to size.

Related Specifications

1.4401 1.4404 BS EN 10088-1 X2CrNiMo17-12-2 AISI ASTM


Analysis
Carbon*0.08% maxChromium16.00-18.00%
Manganese2.00% maxNickel10.00-14.00%
Silicon1.00% maxMolybdenum2.00-3.00%
Sulphur0.03% max

Phosphorous0.03% max

(*Carbon content on 316L 0.03% max)


Form of Supply

TISCO Steel are suppliers and stockholders of round bar, plate and sheet. Sawn blanks can be supplied cut to your requirements as one offs or multiple cut pieces. Ground 316 bar can be supplied, providing a high quality precision ground bar to close tolerances. Also available in plate which can be supplied as 316 plasma cut pieces and sheet which can be supplied guillotined to size. 





SheetPlateDiameter

Applications

Used widely in industries such as chemical, construction, aerospace and automotive. Typical applications are exhaust manifolds, heat exchangers, bellows, oil refinery equipment, marine equipment, pulp paper and textile processing equipment.


Corrosion Resistance

316 stainless steel grade is more resistant to atmospheric and other mild types of corrosion than that of other austenitic stainless steel grades, such as 303, 304, 321 and 310. As a molybdenum bearing stainless it is considerably more resistant to solutions of sulphuric acid and phosphoric acid than that of other austenitic grades. 316 has a better resistance to pitting corrosion and stress corrosion cracking in chloride solutions to that of other non molybdenum bearing stainless steel grades.


Welding

Stainless steel 316 is readily weldeable with most welding procedures. Oxyacetylene welding is not recommended due to possible carbon pick up in the weld area. With its lower carbon content 316L stainless is preferred to standard 316 as it can be welded without loss of corrosion resistance due to intergranular carbide precipitation. Post weld annealing is not normally required, except for service in more extreme conditions. We recommend you contact your welding consumables supplier who should provide you full assistance and information on welding stainless steel.


Forging

Heat the 316 slowly and uniformly throughout the section to 1150-1200°C. Re heat as necessary and avoid working below 900°C. Cool in air. Forgings will require annealing in order to obtain optimum corrosion resistance.


Scaling Temperature

The oxidation resistance of a stainless steel specification is traditionally termed as the scaling temperature. This is the temperature at which the oxidation rate of a stainless steel becomes unacceptably high. The safe scaling temperature for continuous service of 316 is 875°C. In an oxidising and reducing sulphurous atmosphere the scaling temperature of 316 stainless is lowered.


Typical Physical Properties
Temp °C


Density 

Kg/m³
 

Mean Coefficient

of Thermal Expansion
 

Modulus 
of Elasticity

kg/mm

Electrical
Resistivity
Ωmm²/m
Specific Heat
Capacity

kcalºC

209.0016.5x10-6200000.750.105

Certification

Stainless steel 316 grade is available with BS EN 10204 3.1 mill certificate, please request when placing any orders.


Quality Assured Supply

316 stainless is supplied in accordance with our ISO 9001 : 2008 registration.